Aluminium 3003 Sheet is made up of a commercially pure aluminum material that has high mechanical properties. Stancor Alloys is a supplier and distributor of the 3003 Aluminium Plates in different forms and dimensions. The material has a medium strength compared to most metallic alloys. The 3003 Aluminium Hot Rolled Plate also has very good corrosion resistance to atmospheric components. The material has improved mechanical properties compared to the other grades of aluminum. The Aluminium 3003 Chequered Plate and others can be worked upon. They have good formability and machinability. The applications of the material are in chemical equipment manufacturing, cooking and kitchen appliances, heat exchangers and in storage tanks. The ASTM B209 Aluminum Alloy 3003 Plates have 98.6% aluminum in the composition with manganese and copper included.
The composition allows the 3003 Aluminium HR Plate to have high temperature capabilities. The melting point of the material is 644 degrees Celsius. And the density of the Aluminium 3003 Perforated Sheets is 2.73 grams per cubic centimeter. The material also has good tensile strength with minimum130MPa and minimum 125MPa yield strength. It has 55MPa fatigue strength and the Aluminium 3003 Coils have 83MPa shear strength as well. They have good elongation and elastic modulus values with hardness. The hardness is 35BNH for the ASME SB209 Aluminium 3003 Sheets. The applications include eyelet stock, awning slats, garage doors, storage tanks, ice cube trays, cooking utensils and many more. There are different forms such as strips, coils, foils and Aluminium 3003 Circle in this grade of material. Please feel free to contact us for more information on the product and the 3003 Aluminium CR Sheets prices.
Table of Content - 3003 Aluminium HR Plate Specification And Material Grade - Aluminium 3003 Plate Chemical Composition Chart - Aluminium DIN 3.0517 Sheets Mechanical Strength Table - Basic Types Of Aluminium 3003 Sheet - Equivalent Grades Of Aluminium 3003 Coils - ASTM B209 Aluminum Alloy 3003 Plates Weight Chart
|Standards||ASTM B209 / ASME SB209|
|Surface||Bright, polished, hair line, brush, sand blast, checkered, embossed, etching, etc.|
|Temper||O, F, H12, H14, H16, H18, H19, H22, H24, H26, H32, H34, H36, H38, H111, H112, H321, T3, T4, T5, T6, T7, T351, T451, T651, T851|
|Finish||Mill, Customer specific finish|
|Type||Hot-Rolled (HR) / Cold-Rolled (CR) Sheet / Plates/ Strips/ Coils/ Chequered Plates|
|Aluminum Sheet/ Plate Coating||PVC Coated, Color Coated, Polyester, Fluorocarbon, polyurethane and epoxy coating|
|1.0 to 1.5%||Remainder||0.7%||0.05 to 0.20%||0.6%||0.15%||0.10%|
|Tensile strength||18855 psi||130 MPa|
|Yield strength||18130 psi||125 MPa|
|Shear strength||12039 psi||83 MPa|
|Fatigue strength||7977 psi||55 MPa|
|Elastic modulus||10153-11603 ksi||70-80 GPa|
|European Standard||UNS||OLD||ISO||WNr||GERMANY (DIN)||USA (AA)|