PED Certified EN10028-3 P355NL2 Steel Sheet, P355NL2 Mill Plate Manufacturer in Mumbai

P355NL2 Steel Plates is intended for low temperature applications of pressure vessels and fine grain steels applications. Stancor Alloys is a leading supplier and manufacturer of these materials in large quantities. The EN10028-3 P355NL2 plates is made up of a composition  that has vanadium, titanium, nickel, niobium, molybdenum, copper, chromium, nitrogen, aluminum, sulfur, phosphorus, manganese, silicon and carbon in it. This combination allows the P355NL2 Mill Plates to withstand mild temperatures and to possess high strength values. The material is also easily formable and readily weldable.

The EN10028-3 Grade P355NL2 Plates comes in different thicknesses. The plates range from 5mm to 300mm in thickness. The low thickness plates have high strength values of 355MPa minimum yield strength and up to 630MPa of minimum tensile strength. The EN10028 P355NL2 plates has up to 325MPa minimum yield strength when they are over 50mm in thickness. The plates are also made in different lengths ranging from 3000mm to 15000mm and widths ranging from 1500mm to 4050mm. The EN10028-3 Gr P355 NL2 Plates are resistant to brittle cracking or embrittlement. The applications include storage tanks for pressurized gases. The plates and sheets could also be used in chemical, petrochemical and in oil and gas industrial applications. Please contact us to know more about the plates and their pricing.

EN10028-3 Grade P355NL2 Plates Size Standard And Specification

Width Up to 3 metres
Certificate EN 10204 3.1 /3.2
Length Up to 12 metres
Thickness 6 – 200 milimeter
Number 1.1106

EN10028-3 Grade P355NL2 Plate and Sheet Supplier In Mumbai, India

P355NL2 Mill Plates Chemical Composition Table

Grade The Element Max (%)
Mn Si P C Al(min) S N
P355NL2 0.9-1.70 0.50 0.025 0.18   0.015 0.02
Mo Cu Nb Cr Ti Ni V
0.08 0.30 0.005 0.30 0.03 0.50 0.10

Carbon Equivalent: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

Steel Grade P355NL2 Plates Mechanical Analysis

 

We provide Stockist Of EN10023-3 P355NL2 Pressure Vessel Steel Plates and Sheets with instant delivery.

Grade   P355NL2 Mechanical Property
Thickness Elongation Yield Tensilmie Impact Energy(KV J) min
P355NL2 mm Min  % Min Mpa Mpa -20° +20°
≤ 16 22 355 490-630 65 90 100
16> to ≤35 22 355 490-630 65 90 100
35> to ≤50 22 345 490-630 65 90 100
50> to ≤70 22 325 490-630 65 90 100
70> to ≤100 21 315 470-610 65 90 100
100> to ≤150 21 295 450-590 65 90 100

Equivalent Of EN10028-3 P355NL2 Plates

 
Accept all small/ Large Orders BS EN 10028 3 P355NL2 Carbon Steel Plates Weight Chart and Equivalent.
Germany Belgium France Europe Sweden Italy India Japan
E St E355         Fe510-2-KG    

What Are The Different Types Of P355NL2 Plates?

Manufacture of Grade P355NL2 Steel Plates In Mumbai, India.
EN10028-3 P355NL2 Steel Plate EN10028-3 P355NL2 Steel Plate
P355NL2 Mill Plate P355NL2 Mill Plate
EN10028-3 Grade P355NL2 Plate EN10028-3 Grade P355NL2 Plate
EN10028 P355NL2 Steel Plate EN10028 P355NL2 Steel Plate
EN10028-3 Grade P355NL2 Steel Plates EN10028-3 Grade P355NL2 Steel Plates
EN10023-3 P355NL2 Pressure Vessel Steel Plates EN10023-3 P355NL2 Pressure Vessel Steel Plates
EN10028 P355NL2 Steel Sheet EN10028 P355NL2 Steel Sheet
EN 10028 3 P355NL2 Carbon Steel Plate EN 10028 3 P355NL2 Carbon Steel Plate
P355NL2 Material P355NL2 Material
BS EN10028-3 p355nl2 Sheet BS EN10028-3 p355nl2 Sheet
P355NL2 EN 10028-3 Plate P355NL2 EN 10028-3 Plate
Steel Grade P355NL2 Plate Steel Grade P355NL2 Plate

EN 10028-2 P355NL2 Plates Technical Requirements

  • High tension test
  • Low temperature impacting test
  • Simulated post-welded heat treatment (PWHT)
  • Ultrasonic test under EN 10160,ASTM A435,A577,A578
  • Issued Orginal Mill test certificate under EN 10204 FORMAT 3.1/3.2
  • Shot blasting and Painting,Cutting and welding as per end user’s demands

Application of P355 NL2 Plates

  • Boilers
  • Calorifiers
  • Columns
  • Dished Ends
  • Filters
  • Flanges
  • Heat exchangers
  • Pipelines
  • Pressure vessels
  • Storage tanks
  • Valves

EN 10028-2 P355NL2 Plates Processing

  • Cutting
  • Forming Drilling/ Machining
  • Grinding
  • Testing

P355NL2 Plates Impact Test

  Type Usual
Dekivery
Condition
Norminal
Thickness
(mm)
Impact Energy KV min[J] at temperature [°C]
Longitudinal Longitudinal
-50 -40 -20 0 +20 -50 -40 -20 0 +20
P355NL1 N 5-150 27 34 47 55 63 16 20 27 34 40

P355 NL2 Steel Plate Material Testing

  • Pitting Resistance Test
  • Flattening Test
  • Chemical Analysis – Spectro Analysis
  • Flaring Test
  • Hardness Test
  • Positive Material Identification – PMI Testing
  • Mechanical Testing Such as Tensile of Area
  • Micro and MacroTest
  • Intergranular Corrosion (IGC) Test